Title: Degree of phase transformations in the conditions of polythermal synthesis of SrBaFeMoO6–δ
Authors: Kalanda, N. A.
Yarmolich, M. V.
Kutuzau, M.
Gurskii, A. L.
Maria do Rosario Teixeira Soares
Mindaugas Andrulevicius
Brigita Abakeviciene
Sigitas Tamulevicius
Keywords: публикации ученых;Magnetic metal oxide compound;Double perovskite;Polythermal synthesis;Differential thermal analysis;Thermogravimetric analysis
Issue Date: 2020
Publisher: Elsevier
Citation: Degree of phase transformations in the conditions of polythermal synthesis of SrBaFeMoO6–δ / Kalanda N. [et al.] // Vacuum. – 2020. – Vol. 174(4). – P. 109196.
Abstract: The sequence of phase transformations during the crystallization of SrBaFeMoO6 –δ by the solid-phase technique from a stoichiometric mixture of simple oxides SrCO3 þ BaCO3 þ 0.5Fe2O3 þ MoO3 was studied. It has been established that the synthesis of barium – strontium ferromolybdate proceeds through a series of sequential - parallel stages. It was found that to minimize the effect of intermediate reaction products, it is necessary to use combined synthesis modes. As a result of using combined synthesis modes for annealing for 20 h and T ¼ 1443 K in vacuum of 10 5 Torr at the pressure of residual oxygen gas 10 8 Pa, it was possible to obtain a single-phase barium – strontium ferromolybdate compound with superstructural ordering of iron and molybdenum cations.
URI: https://libeldoc.bsuir.by/handle/123456789/43080
Appears in Collections:Публикации в зарубежных изданиях

Files in This Item:
File Description SizeFormat 
Kalanda_Degree.pdf413.01 kBAdobe PDFView/Open
Show full item record Google Scholar

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.